UNS C70610 copper nickel alloy|C70610 copper nickel plate

UNS C70610 copper nickel alloy|C70610 copper nickel |C70610 plate|C70610 sheet
 
United iron and steel limited could manufacture and export Copper Nickel alloys plate and sheet C70100 C70200 C70230 C70240 C70250 C70260 C70265 C70270 C70280 C70290 C70310 C70350 C70370 C70400 C70500 C70600 C70610 C70620 C70690 C70700 C70800 C71000 C71100 C71300 C71500 C71520 C71580 C71581 C71590 C71640 C71700 C71900 C72150 C72200 C72420 C72500 C72650 C72700 C72800 C72900 C72950 Copper Nickel alloys if you have any need in cooper, please contact us by email address: sales@unitedsteelplate.com
 
C70610 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C70610 Chemical Composition

Coppers Nominal Chemical Composition %
Copper	Cu	Pb	Fe	Zn	Ni	Sn	Mn
C70610	Rem	0.01	1-2		10-11		0.5-1
Designation: copper Nickel alloys
Note: Composition percent maximum unless shown as a range or a minimum

(1) : Cu + Sum of Named Elements, 99.5% min.
(2) : Ni value includes Co.
(3) : Ag Includes B
(4) The following additional maximum limits shall apply: .02% C, .015% Si, .003% S, .002% Al, .001% P, .0005%Hg, .001% Ti, .001% Sb, .001% As, .001% Bi, .05% Co, .10% Mg and .005% Oxygen. For C70690, Co shall be .02% max.
(5) : The following additional maximum limits shall apply: .07% C, .15% Si, .024% S, .05% Al and .03% P.
(6) : .02% P, max.; .25% Si, max.; .01% S, max.; .02 - .50% Ti.
(7) The following additional maximum limits shall apply: When the product is for subsequent welding applications and is so specified by the purchaser, .50% Zn, .02% P, .02% Pb, .02%S and .05% C.
(8) : Cu + Sum of Named Elements, 99.8% min.
(9) : Cu + Sum of Named Elements, 99.7% min.
(10) : .005% Pb, max., for hot rolling.
C70610 Properties

C70610 Properties		C70610 Conditions
		T (°C)	Treatment
Density (×1000 kg/m3)
Poisson's Ratio
Elastic Modulus (GPa)
Tensile Strength (Mpa)			(flat products, wire, rod, shapes, tube)
Yield Strength (Mpa)
Elongation (%)
Reduction in Area (%)
Note: Elongation is measured in 5 inches.

 
C70610 Copper supplied Specification:

Coppers C70610	Hot Rolled Coppers plate			Cold Rolled Coppers plate
	Thickness mm	Width mm	Length mm	Thickness mm	Width mm	Length mm
Red Copper	6-15	400-3000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-3000		0.5-2.5	600-1000	1000-2500
	21-50	600-3000		3-10	600-2500	1000-3000
	>10-110	600-1000
Yellow Brass	6-15	400-2000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-2000		0.5-2.5	400-1000	1000-3000
	>60	600-2500		3-10	600-2000	1000-2500
Bronze	>2.5	600-1000	1000-6000	0.4-0.49	300-500	600-1500
				0.5-2.5	500-600	1000-3000
				3-10	500-1000	600-2000
Cupronickel	>2.5	400-1500	1000-6000	0.5-2.5	300-600	600-1500
				3-10	300-1000	600-1500

 

















C70610 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C70610 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C70610 Equivalent Grade for Copper alloy

Equivalent Grade for Copper alloy
GB	DIN		EN		ISO	UNS	JIS
	KRUZZEICHEN	NUMBER	Symbol	Number	Symbol	Number	Number
-	-	-	-	-	-	C70610	-

 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C70610 Copper alloy material; please contact us by email sales@unitedsteelplate.com