UNS C96800 Copper plate|C96800 copper sheet|C96800 alloy

Come from:United Iron and Steel Limited  Editor:United Iron and stee Access:

UNS C96800 Copper plate|C96800 copper sheet|C96800 alloy
 
United iron and steel limited manufacture and export Copper Nickel plate C96200 C96300 C96400 C96600 C96700 C96800 C96900 C96950 C96970. If you have any need in cooper, please contact us by email address: sales@unitedsteelplate.com
 
C96800 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C96800 Chemical Composition
Coppers Nominal Chemical Composition %
Copper
C96800
Cu Pb Fe Ni Mn Mn Si Nb C
     Rem 0.005 0.5 9.5-10.5 0.05-0.3   0.05 0.1-0.3  
 Be                
                 
Designation: Copper aluminum iron and copper aluminum iron nickel plate  
Note: Composition percent maximum unless shown as a range or a minimum
(1) : Cu + Sum of Named Elements, 99.5% min.
(2) : Ni value includes Co.
(3) : When product or casting is intended for subsequent welding applications, and so specified by the purchaser, the Nb content shall be .40% max.
(4) : The following additional maximum impurity limits shall apply: .10% Al, .001% B, .001% Bi, .005% P, .0025% S, .02% Sb, .01%Ti.
 
C96800 Properties
C96800 Properties C96800 Conditions
T (°C) Treatment
Density (×1000 kg/m3)      
Poisson's Ratio      
Elastic Modulus (GPa)      
Tensile Strength (Mpa)     (flat products, wire, rod, shapes, tube)
Yield Strength (Mpa)  
Elongation (%)  
Reduction in Area (%)  
Note: Elongation is measured in 5 inches.
 
C96800 Copper supplied Specification:
Coppers
C96800
Hot Rolled Coppers plate Cold Rolled Coppers plate
Thickness mm Width mm Length mm Thickness mm Width mm Length mm
Red Copper 6-15 400-3000 1000-6000 0.2-0.49 300-600 1000-1500
16-20 400-3000 0.5-2.5 600-1000 1000-2500
21-50 600-3000 3-10 600-2500 1000-3000
>10-110 600-1000      
Yellow Brass 6-15 400-2000 1000-6000 0.2-0.49 300-600 1000-1500
16-20 400-2000 0.5-2.5 400-1000 1000-3000
>60 600-2500 3-10 600-2000 1000-2500
Bronze >2.5 600-1000 1000-6000 0.4-0.49 300-500 600-1500
0.5-2.5 500-600 1000-3000
3-10 500-1000 600-2000
Cupronickel >2.5 400-1500 1000-6000 0.5-2.5 300-600 600-1500
3-10 300-1000 600-1500
 
C96800 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C96800 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C96800 Equivalent Grade for Copper alloy
Equivalent Grade for Copper alloy
GB DIN EN ISO UNS JIS
  KRUZZEICHEN NUMBER Symbol Number Symbol Number Number
- - - - - - C96800 -
 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C96800 Copper alloy material; please contact us by email sales@unitedsteelplate.com