UNS C96200 Copper plate|C96200 copper sheet|C96200 alloy

UNS C96200 Copper plate|C96200 copper sheet|C96200 alloy
 
United iron and steel limited manufacture and export Copper Nickel plate C96200 C96300 C96400 C96600 C96700 C96800 C96900 C96950 C96970. If you have any need in cooper, please contact us by email address: sales@unitedsteelplate.com
 
C96200 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C96200 Chemical Composition

Coppers Nominal Chemical Composition %
Copper C96200	Cu	Pb	Fe	Ni	Mn		Si	Nb	C
	Rem	0.01	1-1.8	9-11	1.5		0.5	1.0	0.1
	Be
Designation: Copper aluminum iron and copper aluminum iron nickel plate
Note: Composition percent maximum unless shown as a range or a minimum

(1) : Cu + Sum of Named Elements, 99.5% min.
(2) : Ni value includes Co.
(3) : When product or casting is intended for subsequent welding applications, and so specified by the purchaser, the Nb content shall be .40% max.
(4) : The following additional maximum impurity limits shall apply: .10% Al, .001% B, .001% Bi, .005% P, .0025% S, .02% Sb, .01%Ti.
 
C96200 Properties

C96200 Properties		C96200 Conditions
		T (°C)	Treatment
Density (×1000 kg/m3)
Poisson's Ratio
Elastic Modulus (GPa)
Tensile Strength (Mpa)			(flat products, wire, rod, shapes, tube)
Yield Strength (Mpa)
Elongation (%)
Reduction in Area (%)
Note: Elongation is measured in 5 inches.

 
C96200 Copper supplied Specification:

Coppers C96200	Hot Rolled Coppers plate			Cold Rolled Coppers plate
	Thickness mm	Width mm	Length mm	Thickness mm	Width mm	Length mm
Red Copper	6-15	400-3000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-3000		0.5-2.5	600-1000	1000-2500
	21-50	600-3000		3-10	600-2500	1000-3000
	>10-110	600-1000
Yellow Brass	6-15	400-2000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-2000		0.5-2.5	400-1000	1000-3000
	>60	600-2500		3-10	600-2000	1000-2500
Bronze	>2.5	600-1000	1000-6000	0.4-0.49	300-500	600-1500
				0.5-2.5	500-600	1000-3000
				3-10	500-1000	600-2000
Cupronickel	>2.5	400-1500	1000-6000	0.5-2.5	300-600	600-1500
				3-10	300-1000	600-1500

 
C96200 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C96200 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C96200 Equivalent Grade for Copper alloy

Equivalent Grade for Copper alloy
GB	DIN		EN		ISO	UNS	JIS
	KRUZZEICHEN	NUMBER	Symbol	Number	Symbol	Number	Number
-	-	-	-	-	-	C96200	-

 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C96200 Copper alloy material; please contact us by email sales@unitedsteelplate.com