UNS C94400 Bronze plate|C94400 Bronze sheet|C94400 Tin Bronze
 
United iron and steel limited manufacture and export High Leaded tin bronze plate C93100 C93200 C93400 C93500 C93600 C93700 C93720 C93800 C93900 C94000 C94100 C94300 C94310 C94320 C94330 C94400 C94500 Tin Bronzes. If you have any need in cooper, please contact us by email address: sales@unitedsteelplate.com
 
C94400 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C94400 Chemical Composition

Coppers Nominal Chemical Composition %
Copper C94400	Cu	Sn	Pb	Zn	Fe	Sb	Ni	S	P
	Rem	7-9	9-12	0.8	0.15	0.8	1.0	0.08	0.5
	Al	Si
	0.005	0.005
Designation: Tin Bronzes Copper Tin Alloy
Note: Composition percent maximum unless shown as a range or a minimum

(1) : Cu + Sum of Named Elements, 99.3% min.
(2) : In determining Cu min., Cu may be calculated as Cu + Ni.
(3) : Ni value includes Co.
(4) : For continuous castings, P shall be 1.5%, max.
 
C94400 Properties

C94400 Properties		C94400 Conditions
		T (°C)	Treatment
Density (×1000 kg/m3)
Poisson's Ratio
Elastic Modulus (GPa)
Tensile Strength (Mpa)			(flat products, wire, rod, shapes, tube)
Yield Strength (Mpa)
Elongation (%)
Reduction in Area (%)
Note: Elongation is measured in 5 inches.

 
C94400 Copper supplied Specification:

Coppers C94400	Hot Rolled Coppers plate			Cold Rolled Coppers plate
	Thickness mm	Width mm	Length mm	Thickness mm	Width mm	Length mm
Red Copper	6-15	400-3000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-3000		0.5-2.5	600-1000	1000-2500
	21-50	600-3000		3-10	600-2500	1000-3000
	>10-110	600-1000
Yellow Brass	6-15	400-2000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-2000		0.5-2.5	400-1000	1000-3000
	>60	600-2500		3-10	600-2000	1000-2500
Bronze	>2.5	600-1000	1000-6000	0.4-0.49	300-500	600-1500
				0.5-2.5	500-600	1000-3000
				3-10	500-1000	600-2000
Cupronickel	>2.5	400-1500	1000-6000	0.5-2.5	300-600	600-1500
				3-10	300-1000	600-1500

 
C94400 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C94400 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C94400 Equivalent Grade for Copper alloy

Equivalent Grade for Copper alloy
GB	DIN		EN		ISO	UNS	JIS
	KRUZZEICHEN	NUMBER	Symbol	Number	Symbol	Number	Number
-	-	-	-	-	-	C94400	-

 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C94400 Copper alloy material; please contact us by email sales@unitedsteelplate.com