UNS C61900 Aluminum bronzes|C61900 Aluminum alloy|C61900

UNS C61900 Aluminum bronzes|C61900 Aluminum alloy|C61900 plate|C61900 sheet
 
United iron and steel limited could manufacture and export C60800 C61000 C61300 C61400 C61500 C61550 C61800 C61900 C62200 C62300 C62400 C62500 C62580 C62581 C62582 C63000 C63010 C63020 C63200 C63280 C63380 C63400 C63600 C63800 C64200 C64210 Copper-Aluminum Alloys (Aluminum Bronzes) ,If you have any need in cooper, please contact us by email address: sales@unitedsteelplate.com
 
C61900 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C61900 Chemical Composition

Coppers Nominal Chemical Composition %
Copper	Cu	Pg	Fe	Sn	Zn	AL	Mn	Si	Ni
C61900	Rem	0.02	3.0-4.5	0.6	0.8	8.5-10.0
Designation: Copper-Aluminum Alloys (Aluminum Bronzes)
Note: Composition percent maximum unless shown as a range or a minimum

(1): Cu + Sum of Named Elements, 99.5% min.
(2): Cu + Sum of Named Elements, 99.8% min.
(3): When the product is for subsequent welding applications and is so specified by the purchaser, Cr, Cd, Zr, and Zn shall each be .05%max.
(4): Ni value includes Co.
(5): Fe content shall not exceed Ni content.
(6): Not including Co.
 
C61900 Properties

C61900 Properties		C61900 Conditions
		T (°C)	Treatment
Density (×1000 kg/m3)
Poisson's Ratio
Elastic Modulus (GPa)
Tensile Strength (Mpa)			(flat products, wire, rod, shapes, tube)
Yield Strength (Mpa)
Elongation (%)
Reduction in Area (%)
Note: Elongation is measured in 5 inches.

 
C61900 Copper supplied Specification:

Coppers C61900	Hot Rolled Coppers plate			Cold Rolled Coppers plate
	Thickness mm	Width mm	Length mm	Thickness mm	Width mm	Length mm
Red Copper	6-15	400-3000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-3000		0.5-2.5	600-1000	1000-2500
	21-50	600-3000		3-10	600-2500	1000-3000
	>10-110	600-1000
Yellow Brass	6-15	400-2000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-2000		0.5-2.5	400-1000	1000-3000
	>60	600-2500		3-10	600-2000	1000-2500
Bronze	>2.5	600-1000	1000-6000	0.4-0.49	300-500	600-1500
				0.5-2.5	500-600	1000-3000
				3-10	500-1000	600-2000
Cupronickel	>2.5	400-1500	1000-6000	0.5-2.5	300-600	600-1500
				3-10	300-1000	600-1500

 

















C61900 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C61900 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C61900 Equivalent Grade for Copper alloy

Equivalent Grade for Copper alloy
GB	DIN		EN		ISO	UNS	JIS
	KRUZZEICHEN	NUMBER	Symbol	Number	Symbol	Number	Number
-	-	-	-	-	-	C61900	-

 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C61900 Copper alloy material; please contact us by email sales@unitedsteelplate.com