UNS C55180 Silver Phosphor Bronzes|C55180 Copper alloy

UNS C55180 Silver Phosphor Bronzes|C55180 Copper alloy|C55180 plate|C55180 sheet
 
United iron and steel limited could manufacture and export C55180 C55181 C88281 C55281 C55282 C55283 C55284 C55385 C56000 Copper-Phosphorus and Copper-Silver-Phosphorus Alloy
If you have any need in cooper, please contact us by email address: sales@unitedsteelplate.com
 
C55180 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C55180 Chemical Composition

Coppers Nominal Chemical Composition %
Copper	Cu	Ag	P
C55180	Rem		4.8-5.2			-
Designation: Copper-Phosphorus and Copper-Silver-Phosphorus Alloy
Note: Composition percent maximum unless shown as a range or a minimum

1.Cu + Sum of Named Elements, 99.85% min.
2. Cu + Sum of Named Elements, 99.85% min.
3.:Cu + Sum of Named Elements, 99.5% min.
C55180 Properties

C55180 Properties		C55180 Conditions
		T (°C)	Treatment
Density (×1000 kg/m3)
Poisson's Ratio
Elastic Modulus (GPa)
Tensile Strength (Mpa)			(flat products, wire, rod, shapes, tube)
Yield Strength (Mpa)
Elongation (%)
Reduction in Area (%)
Note: Elongation is measured in 5 inches.

 
C55180 Copper supplied Specification:

Coppers C55180	Hot Rolled Coppers plate			Cold Rolled Coppers plate
	Thickness mm	Width mm	Length mm	Thickness mm	Width mm	Length mm
Red Copper	6-15	400-3000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-3000		0.5-2.5	600-1000	1000-2500
	21-50	600-3000		3-10	600-2500	1000-3000
	>10-110	600-1000
Yellow Brass	6-15	400-2000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-2000		0.5-2.5	400-1000	1000-3000
	>60	600-2500		3-10	600-2000	1000-2500
Bronze	>2.5	600-1000	1000-6000	0.4-0.49	300-500	600-1500
				0.5-2.5	500-600	1000-3000
				3-10	500-1000	600-2000
Cupronickel	>2.5	400-1500	1000-6000	0.5-2.5	300-600	600-1500
				3-10	300-1000	600-1500

 

















C55180 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C55180 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C55180 Equivalent Grade for Copper alloy

Equivalent Grade for Copper alloy
GB	DIN		EN		ISO	UNS	JIS
	KRUZZEICHEN	NUMBER	Symbol	Number	Symbol	Number	Number
-	-	-	-	-	-	C55180	-

 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C55180 Copper alloy material; please contact us by email sales@unitedsteelplate.com