UNS C19500 copper plate|C19500 copper alloy|C19500 sheet

C19500 copper plate|C19500 copper alloy|C19500 sheet
 
United iron and steel limited could produce and supply C19500 C19500 C19500 C19500 C19500 C19500 C19500 C19500 C19500 C19500 C19520 C19700 C19710 C19720 C19750 C198High copper alloys plate
Dispersion: High copper alloys If you need in C19500 copper material, please contact us by email address: sales@unitedsteelplate.com
 
C19500 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C19500 Chemical Composition
 

Coppers Nominal Chemical Composition %
Copper	Cu	Fe	Sn	Zn	Al	Pb	P
C19500	96.0min	1-2	0.1-1.0	0.20	0.02	0.02	0.01-0.35
Designation: High copper alloys Description:
Note: Composition percent maximum unless shown as a range or a minimum

(1) : Cu + Sum of Named Elements, 99.8% min.
(2) : Cu + Sum of Named Elements, 99.9% min.
(3) : Cu + Sum of Named Elements, 99.5% min.
(4) : Ni value includes Co.
 
C19500 Properties

C19500 Properties		C19500 Conditions
		T (°C)	Treatment
Density (×1000 kg/m3)
Poisson's Ratio
Elastic Modulus (GPa)
Tensile Strength (Mpa)			(flat products, wire, rod, shapes, tube)
Yield Strength (Mpa)
Elongation (%)
Reduction in Area (%)
Note: Elongation is measured in 5 inches.

 
C19500 Copper supplied Specification:

Coppers C19500	Hot Rolled Coppers plate			Cold Rolled Coppers plate
	Thickness mm	Width mm	Length mm	Thickness mm	Width mm	Length mm
Red Copper	6-15	400-3000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-3000		0.5-2.5	600-1000	1000-2500
	21-50	600-3000		3-10	600-2500	1000-3000
	>10-110	600-1000
Yellow Brass	6-15	400-2000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-2000		0.5-2.5	400-1000	1000-3000
	>60	600-2500		3-10	600-2000	1000-2500
Bronze	>2.5	600-1000	1000-6000	0.4-0.49	300-500	600-1500
				0.5-2.5	500-600	1000-3000
				3-10	500-1000	600-2000
Cupronickel	>2.5	400-1500	1000-6000	0.5-2.5	300-600	600-1500
				3-10	300-1000	600-1500

 

















C19500 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C19500 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C19500 Equivalent Grade for Copper alloy

Equivalent Grade for Copper alloy
GB	DIN		EN		ISO	UNS	JIS
	KRUZZEICHEN	NUMBER	Symbol	Number	Symbol	Number	Number
-	-	-	-	-	-	C19500	-

 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C19500 Copper alloy material; please contact us by email sales@unitedsteelplate.com