C19200 copper plate|C19200 copper alloy|C19200 sheet

C19200 copper plate|C19200 copper alloy|C19200 sheet
 
United iron and steel limited could produce and supply C19200 C19210 C19215 C19220 C19260 C19280 C19400 C19410 C19450 C19500 C19520 C19700 C19710 C19720 C19750 C198High copper alloys plate
Dispersion: High copper alloys If you need in C19200 copper material, please contact us by email address: sales@unitedsteelplate.com
 
C19200 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C19200 Chemical Composition
 

Coppers Nominal Chemical Composition %
Copper	Cu	Fe	Sn	Zn	Al	Pb	P
C19200	98.5min	0.-1.2		0.20			0.01-0.04
Designation: High copper alloys Description:
Note: Composition percent maximum unless shown as a range or a minimum

(1) : Cu + Sum of Named Elements, 99.8% min.
(2) : Cu + Sum of Named Elements, 99.9% min.
(3) : Cu + Sum of Named Elements, 99.5% min.
(4) : Ni value includes Co.
 
C19200 Properties

C19200 Properties		C19200 Conditions
		T (°C)	Treatment
Density (×1000 kg/m3)
Poisson's Ratio
Elastic Modulus (GPa)
Tensile Strength (Mpa)			(flat products, wire, rod, shapes, tube)
Yield Strength (Mpa)
Elongation (%)
Reduction in Area (%)
Note: Elongation is measured in 5 inches.

 
C19200 Copper supplied Specification:

Coppers C19200	Hot Rolled Coppers plate			Cold Rolled Coppers plate
	Thickness mm	Width mm	Length mm	Thickness mm	Width mm	Length mm
Red Copper	6-15	400-3000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-3000		0.5-2.5	600-1000	1000-2500
	21-50	600-3000		3-10	600-2500	1000-3000
	>10-110	600-1000
Yellow Brass	6-15	400-2000	1000-6000	0.2-0.49	300-600	1000-1500
	16-20	400-2000		0.5-2.5	400-1000	1000-3000
	>60	600-2500		3-10	600-2000	1000-2500
Bronze	>2.5	600-1000	1000-6000	0.4-0.49	300-500	600-1500
				0.5-2.5	500-600	1000-3000
				3-10	500-1000	600-2000
Cupronickel	>2.5	400-1500	1000-6000	0.5-2.5	300-600	600-1500
				3-10	300-1000	600-1500

 

















C19200 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C19200 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C19200 Equivalent Grade for Copper alloy

Equivalent Grade for Copper alloy
GB	DIN		EN		ISO	UNS	JIS
	KRUZZEICHEN	NUMBER	Symbol	Number	Symbol	Number	Number
-	-	-	-	-	-	C19200	-

 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C19200 Copper alloy material; please contact us by email sales@unitedsteelplate.com