C11045 copper plate|C11045 copper alloy|C11045 ETP

Come from:未知  Editor:admin Access:

C11045 copper plate|C11045 copper alloy|C11045 |C11045 ETP
 
United iron and steel limited could produce and supply C10100, C10200, C10300, C11010, C11010, C11010, C11010, C11010, C10920, C11010, C11010, C11010, C11010, C11020, C11030, C11040, C11045, C11100, C11300, C11400, C11500, C11600, C11700, C12000 Copper alloy. If any need in that material, please contact us by email address: sales@unitedsteelplate.com
 
C11045 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C11045 Chemical Composition
 
Coppers Nominal Chemical Composition %
Copper Cu(incl Ag) Ag(%)min Ag(Troy oz)min As Sb P Te
C11045 99.90min - - 0.0005 0.0004 - 0.0002
Designation: ETP Description: ETP  
Note: Composition percent maximum unless shown as a range or a minimum
 
1. This is a high conductivity copper which has, in the annealed condition a minimum conductivity of 100% IACS except for Alloy C11045 which has minimum conductivity of 101% IACS.
2.  The following additional impurity maximum limits shall apply: Bi, 1ppm (.0001%); Cd, 1ppm (.0001%); Fe, 10ppm (.0010%); Pb, 5ppm (.0005%); Mn,0.5ppm (.00005%); Ni, 10ppm (.0010%); Se, 3ppm (.0003%); Ag, 25ppm(.0025%);S, 15ppm (.0015%); Sn, 2ppm (.0002%); Zn, 1ppm (.0001%).
3.  Cu is determined by the difference between the impurity total and 100%. The Cu value is exclusive of Ag.
4.  Includes P.
5.  Oxygen and trace elements may vary depending on the process.
6.  The following additional maximum limits shall apply: Se, 2ppm (.0002%); Bi, 1.0ppm (.00010%); Group Total, Te + Se +Bi, 3ppm(.0003%). Sn, 5ppm (.0005%); Pb, 5ppm (.0005%); Fe, 10ppm (.0010%); Ni, 10ppm (.0010%), S, 15ppm (.0015%); Ag, 25ppm (.0025%);Oxygen,100-650ppm (.010-.065%). The total maximum allowable of 65ppm(.0065%) does not include oxygen.
7. These total maximum limits shall apply; Se 2ppm(.0002%); Bi .5ppm (.00005%); Sn 5 ppm (.0005%); Pb 5ppm (.0005%); Fe 10 ppm (.0010%); Ni 10ppm (.0010%); S 15 ppm (.0015%); Ag 25 ppm (.0025%); Oxygen 125 - 600ppm.
8.  Small amounts of Cd or other elements may be added by agreement to improve the resistance to softening at elevated temperatures.
9. Includes B + P.
C11045 Copper supplied Specification:
Coppers
C11045
Hot Rolled Coppers plate Cold Rolled Coppers plate
Thickness mm Width mm Length mm Thickness mm Width mm Length mm
Red Copper 6-15 400-3000 1000-6000 0.2-0.49 300-600 1000-1500
16-20 400-3000 0.5-2.5 600-1000 1000-2500
21-50 600-3000 3-10 600-2500 1000-3000
>10-110 600-1000      
Yellow Brass 6-15 400-2000 1000-6000 0.2-0.49 300-600 1000-1500
16-20 400-2000 0.5-2.5 400-1000 1000-3000
>60 600-2500 3-10 600-2000 1000-2500
Bronze >2.5 600-1000 1000-6000 0.4-0.49 300-500 600-1500
0.5-2.5 500-600 1000-3000
3-10 500-1000 600-2000
Cupronickel >2.5 400-1500 1000-6000 0.5-2.5 300-600 600-1500
3-10 300-1000 600-1500
 


















C11045 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C11045 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, lead, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C11045 Equivalent Grade for Copper alloy
Equivalent Grade for Copper alloy
GB DIN EN ISO UNS JIS
  KRUZZEICHEN NUMBER Symbol Number Symbol Number Number
- - - - - - C11045 -
 
 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C11045 Copper alloy material, please contact us by email sales@unitedsteelplate.com