UNS C63010 Aluminum bronzes|C63010 Aluminum alloy|C63010

Come from:United Iron and Steel Limited  Editor:United Iron and stee Access:

UNS C63010 Aluminum bronzes|C63010 Aluminum alloy|C63010 plate|C63010 sheet
 
United iron and steel limited could manufacture and export C60800 C61000 C61300 C61400 C61500 C61550 C61800 C61900 C62200 C62300 C62400 C62500 C62580 C62581 C62582 C63000 C63010 C63020 C63200 C63280 C63380 C63400 C63600 C63800 C64200 C64210 Copper-Aluminum Alloys (Aluminum Bronzes) ,If you have any need in cooper, please contact us by email address: sales@unitedsteelplate.com
 
C63010 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C63010 Chemical Composition
Coppers Nominal Chemical Composition %
Copper Cu Pg Fe Sn Zn AL Mn Si Ni
C63010 78min   2.0-3.5 0.2 0.3 9.7-10.9 1.5   4.5-5.5
Designation: Copper-Aluminum Alloys (Aluminum Bronzes)  
Note: Composition percent maximum unless shown as a range or a minimum
(1): Cu + Sum of Named Elements, 99.5% min.
(2): Cu + Sum of Named Elements, 99.8% min.
(3): When the product is for subsequent welding applications and is so specified by the purchaser, Cr, Cd, Zr, and Zn shall each be .05%max.
(4): Ni value includes Co.
(5): Fe content shall not exceed Ni content.
(6): Not including Co.
 
C63010 Properties
C63010 Properties C63010 Conditions
T (°C) Treatment
Density (×1000 kg/m3)      
Poisson's Ratio      
Elastic Modulus (GPa)      
Tensile Strength (Mpa)     (flat products, wire, rod, shapes, tube)
Yield Strength (Mpa)  
Elongation (%)  
Reduction in Area (%)  
Note: Elongation is measured in 5 inches.
 
C63010 Copper supplied Specification:
Coppers
C63010
Hot Rolled Coppers plate Cold Rolled Coppers plate
Thickness mm Width mm Length mm Thickness mm Width mm Length mm
Red Copper 6-15 400-3000 1000-6000 0.2-0.49 300-600 1000-1500
16-20 400-3000 0.5-2.5 600-1000 1000-2500
21-50 600-3000 3-10 600-2500 1000-3000
>10-110 600-1000      
Yellow Brass 6-15 400-2000 1000-6000 0.2-0.49 300-600 1000-1500
16-20 400-2000 0.5-2.5 400-1000 1000-3000
>60 600-2500 3-10 600-2000 1000-2500
Bronze >2.5 600-1000 1000-6000 0.4-0.49 300-500 600-1500
0.5-2.5 500-600 1000-3000
3-10 500-1000 600-2000
Cupronickel >2.5 400-1500 1000-6000 0.5-2.5 300-600 600-1500
3-10 300-1000 600-1500
 

















C63010 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C63010 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C63010 Equivalent Grade for Copper alloy
Equivalent Grade for Copper alloy
GB DIN EN ISO UNS JIS
  KRUZZEICHEN NUMBER Symbol Number Symbol Number Number
- - - - - - C63010 -
 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C63010 Copper alloy material; please contact us by email sales@unitedsteelplate.com