C27000 copper Zinc alloy|C27000 yellow brass|C27000 plate

Come from:United Iron and Steel Limited  Editor:United Iron and stee Access:

C27000 copper Zinc alloy|C27000 yellow brass|C27000 plate/sheet
 
United iron and steel limited could produce and supply C21000 C22000 C22600 C23000 C23030 C23400 C24000 C24080 C25600 C26000 C26130 C26200 C26800 C27000 C27200 C27400 C28000 Copper Zinc alloys (Yellow brasses).
Dispersion: yellow brasses, copper zinc alloys, gliding 95%, commercial bronze 90% jewelry bronze, red brass, low brass, cartridge brass, muntz metal. If you need in C21000 copper material, please contact us by email address: sales@unitedsteelplate.com
 
C27000 Copper alloy is usual be used in bus bars, bus conductors, waveguides, hollow conductors, lead-in wires and anodes for vacuum tubes, vacuum seals, transistor components, glass-to-metal seals, coaxial cables, klystrons, microwave tubes, and rectifiers.
 
C27000 Chemical Composition
 
Coppers Nominal Chemical Composition %
Copper Cu Pb Fe Zn      
C27000 63.0-68.5 0.10 0.07       Rem      
Designation: Copper Zinc alloys (Yellow brasses).
Description: yellow brass
 
Note: Composition percent maximum unless shown as a range or a minimum
(1) : Cu + Sum of Named Elements, 99.8% min.
(2) : Cu + Sum of Named Elements, 99.7% min.
 
C27000 Properties
C27000 Properties C27000 Conditions
T (°C) Treatment
Density (×1000 kg/m3)      
Poisson's Ratio      
Elastic Modulus (GPa)      
Tensile Strength (Mpa)     (flat products, wire, rod, shapes, tube)
Yield Strength (Mpa)  
Elongation (%)  
Reduction in Area (%)  
Note: Elongation is measured in 5 inches.
 
C27000 Copper supplied Specification:
Coppers
C27000
Hot Rolled Coppers plate Cold Rolled Coppers plate
Thickness mm Width mm Length mm Thickness mm Width mm Length mm
Red Copper 6-15 400-3000 1000-6000 0.2-0.49 300-600 1000-1500
16-20 400-3000 0.5-2.5 600-1000 1000-2500
21-50 600-3000 3-10 600-2500 1000-3000
>10-110 600-1000      
Yellow Brass 6-15 400-2000 1000-6000 0.2-0.49 300-600 1000-1500
16-20 400-2000 0.5-2.5 400-1000 1000-3000
>60 600-2500 3-10 600-2000 1000-2500
Bronze >2.5 600-1000 1000-6000 0.4-0.49 300-500 600-1500
0.5-2.5 500-600 1000-3000
3-10 500-1000 600-2000
Cupronickel >2.5 400-1500 1000-6000 0.5-2.5 300-600 600-1500
3-10 300-1000 600-1500
 


















C27000 Processing and Property:  Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.
 
C27000 Corrosion Resistance: Good to excellent. Susceptible to galvanic corrosion when coupled with iron, aluminum, magnesium, leads, tin, and zinc. Good resistance to atmospheric, brackish water, sea water, and non-oxidizing acid corrosion, but avoid heating in oxidizing atmospheres or exposing to oxidizing acids, moist halogens, sulfides, ammonia, or solutions with ammonium ions.
 
C27000 Equivalent Grade for Copper alloy
Equivalent Grade for Copper alloy
GB DIN EN ISO UNS JIS
  KRUZZEICHEN NUMBER Symbol Number Symbol Number Number
- - - - - - C27000 -
 
United iron and steel limited also have stock sizes at our warehouse, if you have requirement in C27000 Copper alloy material; please contact us by email sales@unitedsteelplate.com